Characterization Of Nano-structured Magnesiumchromium ferrites Synthesized By Citrate-gel auto Combustion Method

M. Raghasudha, D. Ravinder, P. Veerasomaiah

Volume 4, Issue 12, Page 910-916, Year 2013 | DOI: 10.5185/amlett.2013.5479

Keywords:

Nano-ferrites; citrate-gel auto combustion; X-ray diffraction; SEM; EDS; FTIR. 

Abstract: 

 Nano-ferrites of the composition Mg Crx Fe2-xO4 (where x=0.0, 0.1, 0.3, 0.5, 0.7, 0.9 and 1.0) were synthesized at a very low temperature (180°C) by Citrate-gel auto combustion method. The as synthesized powders were sintered at 5000C for four hours in an air and were characterized by X-ray diffraction (XRD) which confirmed the formation of cubic spinel structure of ferrites. The crystallite size was in the range of 7 to 23nm for different compositions with the significant decrease of ~16nm in response to the increase in Cr substitution. Such low nano sized ferrites are desirable for variety of applications like, in magnetic data storage and in targeted drug delivery, etc. Morphological studies by Scanning Electron Microscopy (SEM) revealed formation of largely agglomerated, well defined nano particles of the sample. Elemental composition characterizations of the prepared samples were performed by Energy Dispersive Spectroscopy (EDS) which shows the presence of Mg, Cr, Fe and O without precipitating cations. The FTIR spectral studies at room temperature in the range of 400 to 800cm-1 showed two strong absorption bands.  The high frequency band (ν1) around 600 cm-1 is attributed to the intrinsic vibrations of tetrahedral complexes and the low frequency band (ν2) around 400 cm-1 is due to octahedral complexes. The spectra showed the characteristic peaks of ferrite sample.  The observed results can be explained on the basis of composition and crystal size. Copyright © 2013 VBRI press. 