Strength And Microstructure Of Semi-solid Stirring Brazing Of SiCp/A356 Composites And Aluminum Alloy In Air

Huibin Xu, Hui Yang, Quanxiang Luo, Youliang Zeng, Bofang Zhou, Changhua Du

Volume 2, Issue 3, Page 233-238, Year 2011 | DOI: 10.5185/amlett.2011.1216

Keywords:

Aluminum metal-matrix composites; 2024 aluminum alloy; brazing; stirring; semi-solid

Abstract: 

The semi-solid stirring brazing process of SiCp/A356 composites and 2024 aluminum alloy was investigated. The two substrates were heated up to the semisolid temperature range of Zn27Al filler metal in the joint region by a resistance heating plate in air. At this point a stirrer was penetrated into the semi-solid weld seam in order to mix filler metal and the two sides of substrates into a single uniform joint. After stirring, specimens were sectioned for analysis of macro- and micro-structures along the weld region. The research shows that SiCp/A356 composites and aluminum alloy can be successfully joined with semi-solid filler metal by optimizing stirring temperature. It can be found that most of the oxide film on the surface of the base metal was disrupted and removed through the observation by SEM. The metallurgical bonds formed between the filler metal and the base materials. Since the semisolid temperature range of filler metal is narrow, the accurate controlling of weld pool temperature must be considered.Copyright © 2011 VBRI press.

 